Effects of MIG welding Current in Brazing Process on Mechanical Properties and Microstructure of Galvanized Steel Brazing Seam
ประเภทบทความ : บทความวิชาการ
หมวดหมู่ : วิศวกรรมเครื่องกล

Abstract

In this study, the effects of welding currents (ranged from 70, 75, 80, 85, 90 and 95 Amp) on mechanical properties and microstructure of brazing seam from galvanized steel with Copper-Silicon filler by MIG brazing process were reported. It was found that higher welding currents increased the ability of filler penetration into the gap. According to the Microstructures of brazing seam using scanning electron microscopy (SEM), there was precipitation of intermetallic phase (Fe5Si3(Cu)) distributed all over the matrix; while enlargement of Fe5Si3(Cu) was detected at higher welding currents. The presence of the Fe5Si3(Cu) in the brazing seam resulted in an increase in hardness. The strength of brazing seam from every welding current was higher than as-received galvanized steel coupon.

การอ้างอิงบทความ :
วันที่รับบทความ :
วันที่ปรับบทความ :
วันที่ตอบรับ :
วันที่เผยแพร่ออนไลน์ :
วันที่ตีพิมพ์วารสาร :
จำนวนผู้อ่านบทความ : 136

รับข่าวสารจากเรา

รับข่าวสารจากทางเรา ท่านจะสามารถเข้าถึงข่าวสารได้ก่อนใคร แค่เพียงใส่อีเมลของคุณ