Factors of Alkali Solutions Affecting Physical Properties and Microstructure of Fly Ash Geopolymer MortarContaining Portland Cement
ประเภทบทความ : บทความวิชาการ
หมวดหมู่ : วิศวกรรมโยธา
This article investigated the factors of alkali activated solutions affecting mechanical properties and microstructure of fly ash (FA) geopolymer containing Portland cement type I (PC). The PC was used to replace FA at the dosages of 0, 5, 10, 15 and 20% by weight of binder. The alkali activated solution of 10 molar of sodium hydroxide only (NH), 10 molar of sodium hydroxide and sodium silicate solution (NHWG), and sodium silicate solution only (WG) were used as the liquid portion in the mixture. The test results indicated that the type of alkali activated solutions for producing the geopolymer affecting mechanical properties and microstructure of FA geopolymer containing PC. The alkali activators significantly affected the reaction products of geopolymer matrix. The use of NHWG solution gave higher compressive strength and modulus of elasticity of FA geopolymer mortar than those of NH solution only and WG solution only. Moreover, the use of NHWG solution was found to have more peak of calcium silicate hydrate and amorphous phase of FA geopolymer containing PC in XRD pattern than those of NH solution and WG solution only. This was corresponded to SEM results of FA geopolymer paste, which appeared denser and more homogeneous matrix.
วันที่ลง01/07/2019 68

บทความใกล้เคียง

รับข่าวสารจากเรา

รับข่าวสารจากทางเรา ท่านจะสามารถเข้าถึงข่าวสารได้ก่อนใคร แค่เพียงใส่อีเมลของคุณ